The Parylene Coating provides a real conformal protecting layer.
| 1. High crystallinity & molecular weight (~500k) 2. Survives continuous exposure to air at 100°C for l0 years (100,000hrs) 3. Insoluble in any organic solvent up to l50°C 4. Good vacuum stability (weight loss<0.3% under 10-6 torr,50°C) 5. Superior resistance to chemicals & γ-rays. 6. Excellent dielectric properties(Volumn resistivity >8.8 x 1016 ohm-cm) 7. Withstands impacts of more than 100 in-lb at-160ºC 8. Lowest moisture transmission rate (10 times better than epoxy under 90% RH,37ºC) |
| Dimer(DPX) | Monomer(PX) | Polymer(PPX) | |
| 150ºC, 1.0 torr | 680ºC, 0.5 torr | 35ºC, 0.1 torr | -70ºC, 0.001 torr |
| 1. Provide precise thin film coating
(0.2µm to 75µm). 2. Can be coated on almost any material surface. 3. Without curing step that cause no inner stress. 4. Almost no limitation to the complex shape surface. 5. Flamable material can be coated. (ex.paper). 6. Pin hole free coating because no solvent needed. |
abrasion｜backlite｜duracoat｜design｜encap｜force-stroke curve｜plas｜printing｜scs parylene coating｜special rubber part｜terminology
www.joesmen.com.tw
P.O.Box 36-357,Taipei,Taiwan 105,R.O.C﹒
5F-1,No.247,Sec.3 Pa-Teh Road,Taipei,Taiwan l05,R.O.C
Tel:886-2-25794501~3(3 lines)
Fax:886-2-25794601
E-Mail: joesmen@joesmen.com.tw